Long-term environmental goals will motivate the automotive industry, component suppliers, and lubricating oil developers to reduce the friction of their tribosystems to improve overall efficiency and wear for increased component lifetime. Nanoscale ceramic particles have been shown to form a protective layer on components’ surface that reduces wear rate with its high hardness and chemical resistance. One such ceramic is yttria (Y2O3), which has an excellent anti-wear effect, but due to its rarity it would be extremely expensive to produce engine lubricant made from it. Therefore, part of the yttria is replaced by zirconia (ZrO2) with similar physical properties. The study presents the result of the experimental tribological investigation of nanosized yttria–zirconia ceramic mixture as an engine lubricant additive. Yttria-stabilized zirconia (YSZ) nanoparticle was used as the basis for the ratio of the ceramic mixture, so that the weight ratio of yttria–zirconia in the resulting mixture was determined to be 11:69. After the evaluation of the ball-on-disc tribological measurements, it can be stated that the optimal concentration was 0.4 wt%, which reduced the wear diameter by 30% and the wear volume by 90% at the same coefficient of friction. High-resolution SEM analysis showed a significant amount of zirconia on the surface, but no yttria was found.

The continuous tribological development of engine lubricants is becoming more and more vital due to its fuel efficiency improvement and lifetime increasing potential. The antiwear additives play a high role in the lubricants to protect the contacting surfaces even in the presence of thinner oil film. Nanoscale spherical particles in the lubricant may increase the necessary protecting effect. This paper presents the results of the experimental tribological investigation of nanoscale spherical Y2O3 (yttria) ceramic particles as an engine lubricant additive. The ball-on-disc tribological measurements have revealed an optimum concentration at 0.5 wt% with about 45% wear scar diameter and 90% wear volume decrease, compared to the reference, neat Group III base oil. The high-magnitude SEM analysis revealed the working mechanisms of yttria: the particles collected in the roughness valleys resulted in a smoother contacting surface, they were tribo-sintered and they have also caused slight plastic deformation of the outer layer of the metallic surface.